Compilation ya maemo a sebopeho sa lik'hemik'hale sa tšepe lahla likarolo .
Lenaneo 1 Sebopego sa Dikhemikhale (%) GB919- - -67 .
|
Kereiti ya tšhipi . |
C |
Mn . |
SI . |
SP( ka tlase ga goba go lekana le ) . |
||
|
Ⅰ |
Ⅱ |
Ⅲ |
||||
|
ZG15 . |
0.12~0.22 |
0.35~0.65 |
0.20~0.45 |
0.04 |
0.05 |
0.06 |
|
Zg25 . |
0.22~0.32 |
0.50~0.80 |
0.20~0.45 |
0.04 |
0.05 |
0.06 |
|
Zg35 . |
0.32~0.42 |
0.50~0.80 |
0.20~0.45 |
0.04 |
0.05 |
0.06 |
|
ZG45 . |
0.42~0.52 |
0.50~0.80 |
0.20~0.45 |
0.04 |
0.05 |
0.06 |
|
ZG55 . |
0.52~0.62 |
0.50~0.80 |
0.20~0.45 |
0.04 |
0.05 |
0.06 |
ELA HLOKO: Nna —— Tšepe e tsoetseng pele e lahletsoeng; —— boleng bo phahameng ba tšepe e lahletsoeng; —— Tšepe e tlwaelegilego ya go lahlelwa; Nna, goba ga e bontšhwe ka morago ga nomoro ya tšhipi, di tšewa bjalo ka tšhipi ya go lahlelwa ya mphato.
Lenaneo 2 Karolo ya Dikhemikhale GB/T5000.6-1998 ya Tšhipi ya Khapone .
|
Kereiti ya tšhipi . |
Diteng tša elemente ya godimodimo e be e le (%) . |
|||||||||
|
C |
SI . |
Mn . |
S |
P |
Dielemente tša mašaledi . |
|||||
|
Ni n o . |
CR . |
Cu . |
mo . |
V |
||||||
|
ZG200 ~ 4 0 0 0 0 0 0 0 0 0 0 0 0 0 . |
0.20 |
0.50 |
0.80 |
0.04 |
0.04 |
0.30 |
0.35 |
0.30 |
0.20 |
0.05 |
|
ZG230 ~ 4 5 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 |
0.30 |
0.90 |
||||||||
|
ZG270 ~ 5 0 0 0 0 0 0 0 0 0 0 0 . |
0.40 |
|||||||||
|
ZG310 ~ 5 0 0 0 0 0 0 l . |
0.50 |
0.60 |
||||||||
|
Zg340 ~ 6 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 . |
0.60 |
|||||||||
Tšhela:1. Fokotša moedi wa godimo ka 0.01% ya khapone, go dumelela 0{8}}04% ya manganese ya tlaleletšo. Bakeng sa ZG 200 ~ 400 manganese go fihla go 1.00%, mankanese a mane a mane a šetšego a godimo go fihla go 1.20%.
2. Palomoka ya dielemente tša mašaledi e ka se fete 1{2}}00%. ge moreki a sa nyake, dielemente tša mašaledi di ka se sekaseke.
3. Ge sebešo sa esiti se šomišwa go tšweletša di-casting, diteng tša S le P di tla dumelelanwa ke mahlakore ka bobedi.
Lenaneo 3 Sebopego sa Dikhemikhale JB/T5000.6-1998 sa tšhipi ya motswako wa fase .
|
Leina la lebenkele . |
C |
SI . |
Mn . |
P |
S |
CR . |
Ni n o . |
mo . |
Cu . |
|
ZG30MN . |
0.27~0.34 |
0.30~0.50 |
1.20~1.50 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
－ |
－ |
|
|
ZG40MN . |
0.35~0.45 |
0.30~0.45 |
1.20~1.50 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
－ |
－ |
|
|
ZG40MN2. |
0.35~0.45 |
0.20~0.40 |
1.60~1.80 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
－ |
－ |
|
|
ZG50MN2. |
0.45~0.55 |
0.20~0.40 |
1.50~1.80 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
－ |
－ |
|
|
ZG20MN (ZG20Simn) . |
0.12~0.22 |
0.60~0.80 |
1.00~1.30 |
Ka fase ga goba go lekana le 0.035 . |
－ |
Ka fase ga goba go lekana le 0.40 . |
－ |
－ |
|
|
ZG35MN (ZG35SIMN) . |
0.30~0.40 |
0.60~0.80 |
1.10~1.40 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
－ |
－ |
|
|
ZG35SIMNMO . |
0.32~0.40 |
1.10~1.40 |
1.10~1.40 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
0.20~0.30 |
Ka fase ga goba go lekana le 0.30 . |
|
|
ZG35Crmnsi . |
0.30~0.40 |
0.50~0.75 |
0.90~1.20 |
Ka fase ga goba go lekana le 0.035 . |
0.50~0.80 |
－ |
－ |
－ |
|
|
Zg20Mnmo . |
0.17~0.23 |
0.20~0.40 |
1.10~1.40 |
Ka fase ga goba go lekana le 0.035 . |
|
－ |
0.20~0.35 |
Ka fase ga goba go lekana le 0.30 . |
|
|
ZG55Crmnmo (ZG5Crmnmo) . |
0.50~0.60 |
0.25~0.60 |
1.20~1.60 |
Ka fase ga goba go lekana le 0.035 . |
0.60~0.90 |
－ |
0.20~0.30 |
Ka fase ga goba go lekana le 0.30 . |
|
|
ZG40CRL (ZG40CR) . |
0.35~0.45 |
0.20~0.40 |
0.50~0.80 |
Ka fase ga goba go lekana le 0.035 . |
0.80~1.10 |
－ |
－ |
－ |
|
|
ZG34CR2NI2MO (ZG34CrrImo) . |
0.30~0.37 |
0.30~0.60 |
0.60~1.00 |
Ka fase ga goba go lekana le 0.035 . |
1.40~1.70 |
1.40~1.70 |
0.15~0.35 |
－ |
|
|
ZG20CRMO . |
0.17~0.25 |
0.20~0.45 |
0.50~0.80 |
Ka fase ga goba go lekana le 0.035 . |
0.50~0.80 |
－ |
0.40~0.60 |
－ |
|
|
ZG35CRLMO (ZG35CRMO) . |
0.30~0.37 |
0.30~0.50 |
0.50~0.80 |
Ka fase ga goba go lekana le 0.035 . |
0.80~1.20 |
－ |
0.20~0.30 |
－ |
|
|
ZG42CRLMO (ZG42CRMO) . |
0.38~0.45 |
0.30~0.60 |
0.60~1.00 |
Ka fase ga goba go lekana le 0.035 . |
0.80~1.20 |
－ |
0.20~0.30 |
－ |
|
|
ZG50CRLMO (ZG50CRMO) . |
0.46~0.54 |
0.25~0.50 |
0.50~0.80 |
Ka fase ga goba go lekana le 0.035 . |
0.90~1.20 |
－ |
0.15~0.25 |
－ |
|
|
ZG65MN . |
0.60~0.70 |
0.17~0.37 |
0.90~1.20 |
Ka fase ga goba go lekana le 0.035 . |
－ |
－ |
－ |
－ |
|
|
ZG28NICRMO . |
0.25~0.30 |
0.30~0.80 |
0.60~0.80 |
Ka fase ga goba go lekana le 0.035 . |
0.35~0.85 |
0.40~0.80 |
0.35~0.55 |
－ |
|
|
ZG30NICRMO . |
0.25~0.35 |
0.30~0.60 |
0.70~1.00 |
Ka fase ga goba go lekana le 0.035 . |
0.60~0.90 |
0.60~1.00 |
0.35~0.50 |
－ |
|
|
ZG35NICRMO . |
0.30~0.37 |
0.60~0.90 |
0.70~1.00 |
Ka fase ga goba go lekana le 0.035 . |
0.40~0.90 |
0.60~0.90 |
0.40~0.50 |
－ |
|
ELA HLOKO: 1. Palo ka masakaneng ke palo ya setso.2. elements masala Diteng: ni 0{{8} 30%, Cr 0} 0} 30%, Cu 0.25%, MO 0.15%, v 0.05%, palo yohle ya mašaledi a dikarolo 1%. Ge monyakišiši a se na dinyakwa, dielemente tša mašaledi di ka se šomišwe bjalo ka motheo wa kamogelo.
Lenaneo la 4 JB / T7024- - -2002 .
|
Leina la lebenkele . |
C |
Mn . |
SI . |
P |
S |
CR . |
mo . |
V |
|
ZG20CRMO . |
0.15~0.25 |
0.50~0.80 |
0.20~0.60 |
Ka fase ga goba go lekana le 0.030 . |
Ka fase ga goba go lekana le 0.030 . |
0.50~0.80 |
0.40~0.60 |
－ |
|
ZG15CRLMO . |
0.12~0.20 |
Ka fase ga goba go lekana le 0.60 . |
Ka fase ga goba go lekana le 0.025 . |
1.00~1.50 |
0.45~0.65 |
0.20~0.30 |
||
|
ZG15CR2mol . |
0.12~0.18 |
0.40~0.70 |
Ka fase ga goba go lekana le 0.030 . |
2.00~2.75 |
0.90~1.20 |
|||
|
ZG20CrMOV . |
0.18~0.25 |
0.20~0.60 |
0.90~1.20 |
0.50~0.70 |
0.25~0.40 |
|||
|
ZG15CRLMOLV . |
0.12~0.20 |
1.20~1.70 |
0.90~1.20 |
|||||
|
Kgelogelo ye e dumeletšwego . |
±0.02 |
±0.03 |
±0.04 |
±0.005 |
±0.005 |
±0.05 |
±0.03 |
±0.03 |